Synthesis and characterization of Fe6W6C by mechanical alloying

Thumbnail
View/Open
Synthesis and characterization of Fe6W6C by mechanical alloying.png (76.28Kb)
Date
2008-05-23
Author
Barona Mercado, W.
Cuevas, J.
Castro, I. Y.
Fajardo, Marta
Pérez Alcázar, Germán Antonio
Sánchez Sthepa, Héctor
Metadata
Show full item record
Abstract
The properties of the double iron and tungsten carbide prepared by mechanical alloying technique (MA) from elemental powders are reported. The samples were milled for 1, 3, 5, 10, 15, 20, 25 and 30 h. The alloy progress for each milling time was evaluated by X-ray diffraction (XRD) and 57Fe Mössbauer spectrometry. Once the alloy was consolidated two sorts of paramagnetic sites and a magnetic distribution were detected according to the Mössbauer fitting. The majority doublet could correspond to Fe6W6C ternary carbide as X-ray diffraction suggests, and the other could be Fe3W3C. The hyper fine parameters are reported. Vickers microhardness measurements of 30 h milled sample was conducted at room temperature with a load of 0.245 N for 20 s.
URI
https://repository.usc.edu.co/handle/20.500.12421/4368
Collections
  • Artículos Científicos

DSpace software copyright © 2002-2016  DuraSpace
Contact Us | Send Feedback
Theme by 
Atmire NV
 

 

Browse

All of DSpaceCommunities & CollectionsBy Issue DateAuthorsTitlesSubjectsThis CollectionBy Issue DateAuthorsTitlesSubjects

My Account

LoginRegister

Statistics

View Usage Statistics

DSpace software copyright © 2002-2016  DuraSpace
Contact Us | Send Feedback
Theme by 
Atmire NV